It simulates the "worst-case scenario" for parts like O-rings, gaskets, and tires that face sharp edges or localized overstretching during assembly.

It identifies how sensitive a material is to notches or small assembly damage. High values mean a small cut is less likely to cause a total part failure. 📉 Current Status and Successors

: Rubber modulus and tear resistance are highly temperature-dependent; tests are typically standardized at Kremer-tec.de

Since is no longer valid, here is a summary of the correct test method you should be using. This will help you verify if your internal procedures are up to date.